MICROSTRUCTURAL NATURE OF STRENGTHENING OF 12CR18NI10TI STEEL IRRADIATED UP TO 55DPA AFTER POST-IRRADIATION ANNEALINGS
44 56
Abstract
The microstructure changes in 12Cr18Ni10Ti austenitic steel – the material of a spent fuel assembly shroud of the BN-350 reactor – after a series of post-irradiation annealings in the range of 450-1050oC were studied using the transmission electron microscopy. The strengthening of irradiated steel was carried out in the model of dispersed barriers.
References
1. Nikolaeva A.V., Nikolaev Yu.A., Kevorkyan Yu.R. Restoration of Mechanical Properties of Irradiated Steel by Thermal Annealing //Atomic Energy.-2001. -V.90.- N 6.- P. 475-479.
2. Cole J.I., Allen T.R. Microstructural changes induced by post-irradiation annealing of neutron-irradiated austenitic stainless steels // J. Nucl.Mater.- 2000.- V.283-287.- P.329-333.
3. Воеводин В.Н., Неклюдов И.М. Эволюция структурно-фазового состояния и радиационная стойкость конструкционных материалов.- Киев: Наукова Думка, 2006. 375с.
4. Цай К.В., Максимкин О.П., Турубарова Л.Г. Эволюция выделений вторичных фаз при отжиге аустенитной стали 12Х18Н9Т, облученной нейтронами до 5 сна // ФММ.- 2007.- Т.103.- №3.- С.294-302.
5. Higgy H.R., Hommad F.H. Effect of fast-neutron irradiation on mechanical properties of stainless steels: AISI types 304, 316, 347 // J. Nucl. Mater.- 1975.- V.55.- P.177-186.
6. Busby J.T., Hash M.C., Was G.S. The relationship between hardness and yield stress in irradiated austenitic and ferritic steels // J. Nucl. Mater.- 2005.- V. 336.- P.267.-278.
7. Lucas G.E. The evolution of mechanical property change in irradiated austenitic steels // J. Nucl. Mater.- 1993.- V. 206.- P.287.-305.
8. Цай К.В. Микроструктурные исследования стали 12Х18Н10Т, облучавшейся нейтронами в области рефлектора реактора БН-350 // Вестник НЯЦ.- 2008.- Вып.4.- С.88-98.
9. Цай К.В. Оценка радиационного упрочнения стали 12Х18Н10Т – материала чехла отработавшей топливной сборки реактора БН-350 // Хабаршысы - Вестник Каз НТУ.- 2009.-№ 5.- С.36.
10. Porollo S.I., Dvoriashin A.M., Konobeev Yu.V., Ivanov A.A., Shulepin S.V., Garner F.A. Microstructure and mechanical properties of austenitic stainless steel 12X18H9T after neutron irradiation in the pressure vessel of BR-10 fast reactor at very low dose rates // J. Nucl.Mater. -2006.-V.359.-I.1-2.-P.41-49.
11. Максимкин О.П., Цай К.В., Турубарова Л.Г., Силънягина Н.С., Доронина Т.А. Изменение микроструктуры и свойств облученной нейтронами аустенитной стали 12Х18Н10Т в результате пост-радиационных отжигов // Вестник НЯЦ.- 2008.- Вып.4.- С.99-105.
12. Garner F.A., Hamilton M.L., Panayotov N.F. et.al. The microstructural origins of yield strength changes in AISI 316 during fission or fusion irradiation //J. Nucl. Mater.- 1981.- V. 103-104.- P.803-808.
2. Cole J.I., Allen T.R. Microstructural changes induced by post-irradiation annealing of neutron-irradiated austenitic stainless steels // J. Nucl.Mater.- 2000.- V.283-287.- P.329-333.
3. Воеводин В.Н., Неклюдов И.М. Эволюция структурно-фазового состояния и радиационная стойкость конструкционных материалов.- Киев: Наукова Думка, 2006. 375с.
4. Цай К.В., Максимкин О.П., Турубарова Л.Г. Эволюция выделений вторичных фаз при отжиге аустенитной стали 12Х18Н9Т, облученной нейтронами до 5 сна // ФММ.- 2007.- Т.103.- №3.- С.294-302.
5. Higgy H.R., Hommad F.H. Effect of fast-neutron irradiation on mechanical properties of stainless steels: AISI types 304, 316, 347 // J. Nucl. Mater.- 1975.- V.55.- P.177-186.
6. Busby J.T., Hash M.C., Was G.S. The relationship between hardness and yield stress in irradiated austenitic and ferritic steels // J. Nucl. Mater.- 2005.- V. 336.- P.267.-278.
7. Lucas G.E. The evolution of mechanical property change in irradiated austenitic steels // J. Nucl. Mater.- 1993.- V. 206.- P.287.-305.
8. Цай К.В. Микроструктурные исследования стали 12Х18Н10Т, облучавшейся нейтронами в области рефлектора реактора БН-350 // Вестник НЯЦ.- 2008.- Вып.4.- С.88-98.
9. Цай К.В. Оценка радиационного упрочнения стали 12Х18Н10Т – материала чехла отработавшей топливной сборки реактора БН-350 // Хабаршысы - Вестник Каз НТУ.- 2009.-№ 5.- С.36.
10. Porollo S.I., Dvoriashin A.M., Konobeev Yu.V., Ivanov A.A., Shulepin S.V., Garner F.A. Microstructure and mechanical properties of austenitic stainless steel 12X18H9T after neutron irradiation in the pressure vessel of BR-10 fast reactor at very low dose rates // J. Nucl.Mater. -2006.-V.359.-I.1-2.-P.41-49.
11. Максимкин О.П., Цай К.В., Турубарова Л.Г., Силънягина Н.С., Доронина Т.А. Изменение микроструктуры и свойств облученной нейтронами аустенитной стали 12Х18Н10Т в результате пост-радиационных отжигов // Вестник НЯЦ.- 2008.- Вып.4.- С.99-105.
12. Garner F.A., Hamilton M.L., Panayotov N.F. et.al. The microstructural origins of yield strength changes in AISI 316 during fission or fusion irradiation //J. Nucl. Mater.- 1981.- V. 103-104.- P.803-808.
Downloads
How to Cite
Tsay, K. (2018). MICROSTRUCTURAL NATURE OF STRENGTHENING OF 12CR18NI10TI STEEL IRRADIATED UP TO 55DPA AFTER POST-IRRADIATION ANNEALINGS. Recent Contributions to Physics (Rec.Contr.Phys.), 33(2), 80–86. Retrieved from https://bph.kaznu.kz/index.php/zhuzhu/article/view/1044
Issue
Section
Condensed Matter Physics and Materials Science Problems. NanoScience